| Category: | Nylon 410 , Polyamide 410 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | EcoPaXX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GUkAhN_EcoPaXX-Q-KV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EcoPaXX® Q-KV is a Polyamide 410 (Nylon 410) material. It is available in Asia Pacific, Europe, or North America for extrusion or film extrusion. Important attributes of EcoPaXX® Q-KV are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.15 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 1.2 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3500 | 2000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 75.0 | 50.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | |||
| Yield | 4.0 | -- | % | |
| Break | 5.5 | 35 | % |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.2 | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 60 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 190 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 110 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 250 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 6.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | 7.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 32 | 27 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | V-2 | -- | ||
| 1.50 mm | V-2 | -- | ||
| Glow Wire Flammability Index (0.750 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (0.750 mm) | 960 | -- | °C | IEC 60695-2-13 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Biobased Content - Carbon | 62 | -- | % | ASTM D6866 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 255 to 265 | °C | |
| Middle Temperature | 260 to 270 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Nozzle Temperature | 260 to 275 | °C | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4605 TFE 10 FR | RTP Company | SPS | RTP |
| Qenos PP PPV 1762 | Qenos Pty Ltd | PP Copolymer | Qenos PP |
| Sindustris PC GN5152RFA | Sincerity Australia Pty Ltd. | PC+ABS | Sindustris PC |
| CompaMid® PA 6.6 GF 30 HI | DimeLika Plast GmbH | Nylon 66 | CompaMid® |
| 3M™ Dyneon™ PTFE Compound TF 6718 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |