Xuchuan A-9260G/B-6088
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Xuchuan Chemical (Suzhou) Co., Ltd |
| Trademark: | Xuchuan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZoB6g7_Xuchuan-A-9260G-B-6088.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Xuchuan A-9260G/B-6088 is a Thermoplastic Polyurethane Elastomer (Polyester) (TPU-Polyester) product. It is available in Asia Pacific. Typical application: Consumer Goods. Primary characteristic: high hardness. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density | 0.350 to 0.450 | g/cm³ | |
| Density | |||
| A-9260G : 40°C | 1.010 to 1.020 | g/cm³ | |
| B-6088 : 40°C | 1.080 to 1.200 | g/cm³ | |
| Viscosity | |||
| A-9260G : 40°C | 1.00 to 1.40 | Pa·s | |
| B-6088 : 40°C | 0.600 to 0.800 | Pa·s |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| DIN Abrasion | 220 to 300 | mm³ |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Cream Time | 6.0 to 8.0 | sec | |
| End of Rise Time | 50.0 to 60.0 | sec |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Free Rise Foam Density | 170 to 200 | kg/m³ | |
| Preheat Temperature | |||
| Part A | 50 to 60 | °C | |
| Part B | 50 to 60 | °C | |
| Preheat Time | |||
| Part A | 6.0 to 8.0 | hr | |
| Part B | 6.0 to 8.0 | hr | |
| Processing Temperature | |||
| Part A | 40 to 45 | °C | |
| Part B | 38 to 42 | °C |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 50 to 70 |
| Elastomers | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength (Break) | 4.50 to 7.00 | MPa | |
| Tensile Elongation (Break) | 260 to 350 | % | |
| Tear Strength | 18.0 to 30.0 | kN/m |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 86 to 88 | ||
| Demold Time | 5.0 to 7.0 | min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 45.0 to 55.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech AS103 | Shanghai Suptech Engineering Plastics Co. Ltd. | ABS+Nylon | Sup-tech |
| NuSil MED-9021 | NuSil Technology | Silicone | NuSil |
| Expandable PS F11MB | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| KEBAFORM® C 901 CB | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| Plyophen 23041 | Durez Corporation | Phenolic | Plyophen |