RTP 2802-40D
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GPA9pB_RTP-2802-40D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 40 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1240 | MPa | ASTM D638 |
| Tensile Strength | 13.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 896 | MPa | ASTM D790 |
| Flexural Strength | 18.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 370 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 690 | J/m | ASTM D4812 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 6mil/in.Tensile Elongation, ASTM D-638: 8-10% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 177 - 232 | °C | |
| Middle Temperature | 177 - 232 | °C | |
| Front Temperature | 177 - 232 | °C | |
| Mold Temperature | 15.6 - 65.6 | °C | |
| Injection Pressure | 82.7 - 124 | MPa | |
| Back Pressure | 0.345 | MPa | |
| Clamp Tonnage | 4.1 - 8.3 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ProtoCast 19122 | DSM Somos® | Unspecified | ProtoCast |
| Witcom POM-C 2012/300 EXP2 | Witcom Engineering Plastics B.V. | Acetal (POM) Copolymer | Witcom POM-C |
| LOXIM 315 01 HB | LOXIM Industries Private Limited | Nylon 6 | LOXIM |
| Eleme NGP250L | Eleme Petrochemical Company Ltd | PP Homopolymer | Eleme |
| CYCOLOY™ CX7240 resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |