Makrolon® GF9002
| Category: | PC , Polycarbonate |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Makrolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GLzrK7_Makrolon-GF9002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MVR (300 °C/1.2 kg) 15 cm³/10 min; 10 % glass fiber reinforced; flame retardant; UL 94V-0/1.2 mm; low viscosity; easy release; injection molding - melt temperature 310 - 330 °C; available in opaque colors only; electrical/electronic; housing parts with low wall thickness |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.27 | g/cm³ | ISO 1183 |
| Apparent Density 1 | 0.64 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 17 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 2 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.45 | % | |
| Flow : 2.00 mm | 0.50 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.30 | % | |
| Equilibrium, 23°C, 50% RH | 0.10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3900 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 60.0 | MPa | |
| Break, 23°C | 45.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 4.5 | % | |
| Break, 23°C | 10 | % | |
| Flexural Modulus 3(23°C) | 3700 | MPa | ISO 178 |
| Flexural Stress 4 | ISO 178 | ||
| 3.5% Strain, 23°C | 90.0 | MPa | |
| 23°C | 105 | MPa | |
| Flexural Strain at Flexural Strength 5(23°C) | 5.8 | % | ISO 178 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate - US-FMVSS (> 1.00 mm) | passed | ISO 3795 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Shortname | ISO 7391-PC,MFR,(,,)-18-9,GF10 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C, Complete Break) | 8.0 | kJ/m² | ISO 7391 |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C, Complete Break | > 40 | kJ/m² | |
| 23°C, Complete Break | > 100 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy (23°C) | 16.0 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force (23°C) | 3200 | N | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 132 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 141 | °C | ISO 306/B50 |
| -- | 142 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 4.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 6.0E-5 | cm/cm/°C | |
| RTI Elec (0.750 mm) | 80.0 | °C | UL 746 |
| RTI Imp (0.750 mm) | 80.0 | °C | UL 746 |
| RTI Str (0.750 mm) | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 36 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.20 | ||
| 23°C, 1 MHz | 3.20 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 1.0E-3 | ||
| 23°C, 1 MHz | 9.0E-3 | ||
| Comparative Tracking Index | IEC 60112 | ||
| Solution A | 175 | V | |
| Solution B | 125 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-1 | ||
| 1.20 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.750 mm | 960 | °C | |
| 1.50 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 800 | °C | |
| 3.00 mm | 875 | °C | |
| Oxygen Index 7 | 37 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Pellets |
| 2 . | 60x60x2 mm, 500 bar |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2 mm/min |
| 6 . | Based on ISO 179-1eA, 3 mm |
| 7 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTV-2 XP-429 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| Sylvin 8338-80FUV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Chemical Resources BPP400 | Chemical Resources, Inc. | PP Impact Copolymer | Chemical Resources |
| LUVOCOM® 1105-8205 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| Plaslube® PC / ABS 88 GF10 | Techmer Engineered Solutions | PC+ABS | Plaslube® |