| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | AEI Compounds Limited |
| Trademark: | AEI |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GLqkfn_AEI-SX-0620-CM601.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Oil resistant, flexible, halogen free, flame-retardant, silane crosslinkable insulation and sheathing for cable applications This is a flame-retardant, silane crosslinkable, flexible polyolefin compound curable by exposure to moist conditions. The graft component SX-0620 is mixed with a crosslinking catalyst masterbatch CM601 generally in the ratio 97:3. The SX-0620:CM601 compound has been developed to meet the requirements of IEC 92-359 SHF2 and EN50264 EM104 ship wiring and railway standards. The product shows good flexibility and confers tough sheathing protection. CM601catalyst masterbatch is normally added at 3% addition rate. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.48 | g/cm³ | BS 2782 620A |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 2.0 | g/10 min | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 10.0 | MPa | IEC 60811-1-1 |
| Tensile Strain (Break) | 170 | % | IEC 60811-1-1 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength | |||
| 70°C, 168 hr, in IRM 903 oil | -10 | % | |
| 70°C, 168 hr, in water | -20 | % | |
| 100°C, 24 hr, in IRM 902 oil | 7.7 | % | |
| 100°C, 72 hr, in IRM 902 oil | 12 | % | |
| 100°C, 168 hr, in IRM 902 oil | -6.0 | % | |
| 120°C, 168 hr | 12 | % | IEC 60811-1-2 |
| Change in Tensile Strain at Break | |||
| 70°C, 168 hr, in IRM 903 oil | -17 | % | |
| 70°C, 168 hr, in water | -20 | % | |
| 100°C, 24 hr, in IRM 902 oil | -13 | % | |
| 100°C, 72 hr, in IRM 902 oil | 2.1 | % | |
| 100°C, 168 hr, in IRM 902 oil | -2.8 | % | |
| 120°C, 168 hr | -15 | % | IEC 60811-1-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 1 | IEC 60811-2-1 | ||
| Elongation under load, 20N/cm² : 200°C | 60 | % | IEC 60811-2-1 |
| Permanent elongation after cooling | 5.0 | % | IEC 60811-2-1 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Acid Gas Evolution | % | IEC 60754-1 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 160 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 29 | % | ISO 4589-2 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Crosslinking or Cure: A satisfactory cure can also be obtained either by immersion in hot water or exposure to low pressure steam at a temperature up to 70°C. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 100 | °C | |
| Cylinder Zone 2 Temp. | 130 | °C | |
| Cylinder Zone 3 Temp. | 145 | °C | |
| Cylinder Zone 4 Temp. | 155 | °C | |
| Melt Temperature | < 180 | °C | |
| Die Temperature | 165 | °C |
| Extrusion instructions |
|---|
| Many modern thermoplastic extruders will process the material although a screw designed to give good homogenisation without excessive shear (which could cause unacceptable increases in melt temperature) should be used. An extruder with an L/D ratio (length/diameter) of 15-24 and an extruder screw with a compression ratio 1.2:1 to 2:1 are recommended. |
| Note Message | |
|---|---|
| 1 . | Cure assessment by hot set test (forced cured at 80°C in water) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Romiloy® 8150 | ROMIRA GmbH | ASA+PC | Romiloy® |
| TAIRIPRO K4515 | Formosa Plastics Corporation | PP Random Copolymer | TAIRIPRO |
| Boltaron 6800E | Boltaron Performance Products | PMMA+PVC | Boltaron |
| Kynar® 740 | Arkema | PVDF | Kynar® |
| LNP™ STAT-LOY™ PF303 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ STAT-LOY™ |