Ryton® QA220N
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Ryton® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GDXyC5_Ryton-QA220N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ryton® QA220N (granular powder) unfilled polyphenylene sulfide exhibits excellent thermal stability and chemical resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(316°C/5.0 kg) | 160 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.0 | % | |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570 |
| Ash Content | 0.1 | wt% | ISO 3451-1 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Volatiles (150°C) | < 0.3 | wt% |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ISO 527-2 |
| Tensile Stress | 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 3400 | MPa | ISO 178 |
| Flexural Stress | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 3.18 mm | 53 | J/m | ASTM D256 |
| -- | 4.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 160 | °C | |
| 1.8 MPa, Unannealed | 95.0 | °C | |
| Glass Transition Temperature | 90.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | > 180 | °C | ISO 306 |
| Melting Temperature | 280 | °C | ISO 11357-3 |
| CLTE - Flow | ASTM E831 | ||
| -50 to 50°C | 5.0E-5 | cm/cm/°C | |
| 100 to 200°C | 1.2E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.29 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 24 | kV/mm | ASTM D149 |
| Dielectric Constant (25°C, 1 MHz) | 3.20 | ASTM D150 | |
| Dissipation Factor (25°C, 1 MHz) | 2.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Tested by CP Chemical) | V-0 | UL 94 | |
| Oxygen Index | 44 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | Procedure B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X5575 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Manner Flexible PVC M6113 FR | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Shandong Aobang TPU-Polyether 80-A | Shandong Aobang Chemical Technology Co.,Ltd. | TPU-Polyether | Shandong Aobang TPU-Polyether |
| Sypex S1620GB | Ginar Technology Co., LTD. | SAN | Sypex |
| Sylvin 9067-90 Brown 7414 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |