| UV STABILIZED AND IMPACT MODIFIED POLYCARBONATE FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.50 - 0.70 | % | ASTM D955 |
| -- | 0.50 - 0.70 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | > 60.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | > 95 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | > 2200 | MPa | ASTM D790 |
| -- | > 220 | MPa | ISO 178 |
| Flexural Strength | > 90.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 600 | J/m | ASTM D256 |
| 23°C | > 50 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | > 130 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | > 120 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ASTM D1525, ISO 306 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index | 750 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 290 - 310 | °C | |
| Processing (Melt) Temp | 270 - 310 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 70.0 - 107 | MPa | |
| Holding Pressure | 35.0 - 85.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 25 to 50 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Retpol® CA 24 HS UV2 AS | PolyPacific Pty. Ltd. | PP Copolymer | Retpol® |
| NEFTEKHIM PP PP1525J | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| LNP™ LUBRICOMP™ QCP36 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ LUBRICOMP™ |
| LUVOCOM® 19-7330 VP | Lehmann & Voss & Co. | Nylon 46 | LUVOCOM® |
| Sumikon® PM-725 (Type: JZ Black) | SBHPP | Phenolic | Sumikon® |