AXELERON™ GP C-0588 BK CPD

Category:	LDPE , Black Low Density Polyethylene Compound for Cable Jacketing
Manufacturer:	The Dow Chemical Company
Trademark:	AXELERON™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	G4zeVV_AXELERON-GP-C-0588-BK-CPD.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

High voltage low density cable sheath material
AXELERON™GP C- 0588 BK is a high-quality black sheath material for telecommunications cables, containing furnace black. The product has excellent environmental stress cracking resistance, outdoor weather resistance, low temperature performance and extrudable performance. AXELERON™GP C- 0588 BK contains a small amount of anti-dripping additive for the machine head.

Specifications
AXELERON™GP C- 0588 BK meets the following raw material specifications:

ASTM D 1248 IC-5, Grades E5, J1, J3

Federal LP-390C, III-L, Grades 2, 3 and 4, Category 5

REA PE-22, 38, 39, 86, 89, 90

Under the conditions of adopting the correct commercial extruder extrusion processing specifications, use AXELERON™GP C- 0588 BK cable as sheath material should meet the following specifications:

ICEA: S-61-402; NEMA WC5

ANSI: C8. 35

ASTM: D 2308

UK Post Specification M-132G

Telcordia GR 421 Core

ANSI/ICEA S-84-608-1988

General Information
Uses	Telephone lead wire sheath material Cable sheath Wire and cable applications Wire sheath Coaxial cable sheath material
Agency Ratings	ANSI C 8.35 ASTM D 1248, I, Class C, Cat. 5, Grade E5 ASTM D 1248, I, Class C, Cat. 5, Grade J3 FED L-P-390C, Type III, Class L, Category 5, Grade 4 ICEA S-61-402 NEMA WC-5 REA PE-22 REA PE-38 REA PE-39 REA PE-89
Forms	Particle
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.932	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.34	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance (10% Igepal, F20)	> 500	hr	ASTM D1693
Carbon Black Content	2.6	%	ASTM D1603
Absorption Coefficient - (kAB/m)	> 400		ASTM D3349

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638
Yield	10.9	MPa	ASTM D638
--	16.4	MPa	ASTM D638
Tensile Elongation (Break)	700	%	ASTM D638

Electrical	Nominal Value		Test Method
Dielectric Constant (1 MHz)	2.54		ASTM D1531
Dissipation Factor (1 MHz)	2.0E-4		ASTM D1531

Extrusion	Nominal Value	Unit
Melt Temperature	204 - 227	°C

Extrusion instructions
AXELERON™ GP C-0588 BK CPD provides excellent surface finish and outstanding output rates over a broad range of conditions. For optimum results, use melt extrusion temperatures in the suggested range of 400 to 440 °F (204-227°C). Hopper drying at 150-160 °F (67-71°C) to remove moisture is recommended.

Resin Grade	Manufacturer	Category	Trademark
TECHNO ABS 440	Techno Polymer Co, Ltd.	ABS	TECHNO ABS
Siveras™ L304T40	Toray Resin Company	LCP	Siveras™
ULTEM™ 1000F resin	SABIC Innovative Plastics	PEI	ULTEM™
ALCOM® PA66 910/7 GF25 MR15	ALBIS PLASTIC GmbH	Nylon 66	ALCOM® PA66
NORYL GTX™ GTX910 resin	SABIC Innovative Plastics	PPE+PS+Nylon	NORYL GTX™