| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G4zXcQ_DOW-HDPE-DMDA-8940-HEALTH-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Dow HDPE DMDA-8940 HEALTH+™ Resin is a narrow molecular weight distribution high density copolymer designed to offer an excellent balance of toughness, environmental stress crack resistance, and processability. The resin is suitable for injection-molded medical devices such as IV kit components and respiratory care. This product can also be used in pharmaceutical packaging including caps and closures. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.951 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 44 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 26.9 | MPa | ASTM D638 |
| Fracture | 26.9 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.0 | % | ASTM D638 |
| Fracture | 10 | % | ASTM D638 |
| Flexural Modulus - 2% Secant | 1020 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength 1 | 84.1 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 71.1 | °C | ASTM D648 |
| Brittleness Temperature | < -72.2 | °C | ASTM D746 |
| Vicat Softening Temperature | 123 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 128 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 116 | °C | Internal method |
| Additional Information |
|---|
| 根据 ASTM D 4976 进行基板模制和测试。 |
| Note Message | |
|---|---|
| 1 . | Type s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Arnite® TV4 261 /G -99.99.99 | DSM Engineering Plastics | PBT | Arnite® |
| Flontech® FT-GL25-NPA-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| KOPLA PA6 KNP1000F | KOPLA Co., Ltd. | Nylon 6 | KOPLA PA6 |
| LNP™ THERMOCOMP™ AR002XXH compound | SABIC Innovative Plastics | ABS | LNP™ THERMOCOMP™ |
| SABIC® PC PC1003R resin | SABIC Innovative Plastics Asia Pacific | PC | SABIC® PC |