Capilene® T 50
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Carmel Olefins Ltd. |
| Trademark: | Capilene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G3u5xl_Capilene-T-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CAPILENE ® T 50 is a polypropylene homopolymer intended for general purpose injection molding. CAPILENE ® T 50 features: high flow, good stiffness. CAPILENE ® T 50 is suitable for: household articles, closures, rates, containers and garden furniture. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 32.0 | MPa | ASTM D638 |
| Yield | 30.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 2 | 12 | % | ASTM D638 |
| Yield | 12 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 1450 | MPa | ASTM D790 |
| -- 3 | 1400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 23 | J/m | ASTM D256 |
| 23°C | 2.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 97.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 80.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 155 | °C | ISO 306/A, ASTM D1525 4 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 260H | RTP Company | Nylon 66 | RTP |
| ADPOLY EM-520M | Lotte Chemical Corporation | LLDPE | ADPOLY |
| Edgetek™ XT XT-100-BU03 Black | PolyOne Corporation | PC+PBT | Edgetek™ XT |
| POCAN® B 3216 HR 000000 | LANXESS GmbH | PBT | POCAN® |
| LNP™ COLORCOMP™ FR23C compound | SABIC Innovative Plastics | ABS | LNP™ COLORCOMP™ |