CYCOLAC™ INP630 resin
| Category: | ABS+SAN , Acrylonitrile Butadiene Styrene + SAN |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G28mkO_CYCOLAC-INP630-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INP630 is a specialty polymer that increases the service temperature of products. Can be used with a impact modifier to provide impact strength as well as high heat resistance. Provides excellent high heat resistance in thermoplastic polymers. Offers excellent flow properties in outdoor applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/3.8 kg | 11 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 22 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | |||
| 50.0 mm Span 1 | 3880 | MPa | ASTM D790 |
| -- 2 | 3620 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 58.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 3 | 115 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.4 | kJ/m² | ISO 179/2C |
| Notched Izod Impact | |||
| -30°C | 14 | J/m | ASTM D256 |
| 23°C | 19 | J/m | ASTM D256 |
| -30°C 4 | 1.8 | kJ/m² | ISO 180/1A |
| 23°C 5 | 3.2 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 110 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 100 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 6 | 99.6 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 116 | °C | ISO 306/B50 |
| -- | 118 | °C | ISO 306/B120 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yellowness Index | 6.1 | YI | ASTM D1925 |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXT SIGNATURE CAP MG-100 | NEXT Specialty Resins, Inc. | CAP | NEXT SIGNATURE |
| Durepol® PBT A3 G15 TZ NTLA010 BT327 | Petropol Industry and Trade of Polymers LTDA | PBT | Durepol® PBT |
| MAGNUM™ 8391 | Trinseo | ABS | MAGNUM™ |
| Perlast® G75G | Precision Polymer Engineering Ltd. | Perfluoroelastomer | Perlast® |
| Polene LDPE SU 1018 | TPI Polene Public Company Limited | LDPE | Polene LDPE |