PrimaFlex® HI 1402
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Plastic Solutions, Inc. |
| Trademark: | PrimaFlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xEgL9S_PrimaFlex-HI-1402.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Description: HI 1402 is a high melt flow, high impact polystyrene for injection molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 14 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2210 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 22.8 | MPa | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Flexural Strength | 39.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 110 | J/m | ASTM D256 |
| Gardner Impact | 13.6 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 87.2 | °C | ASTM D648 |
| Vicat Softening Temperature | 93.3 | °C | ASTM D1525 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XYRON™ S202A | Asahi Kasei Chemicals Corporation | PPE | XYRON™ |
| Nylene® 4004 HS | Custom Resins Group | Nylon 6 | Nylene® |
| Clariant Nylon 6/6 6608G43-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Orevac® 18507 | Arkema | HDPE | Orevac® |
| Rotuba CAB B9304 (4% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |