PLASTRON™ PP-CF40-11
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | PLASTRON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FzTHtF_PLASTRON-PP-CF40-11.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLASTRON™ PP-CF40-11 is a Polypropylene material filled with 40% carbon fiber. It is available in Asia Pacific. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 160 | MPa | ISO 527-2 |
| Flexural Modulus | 20000 | MPa | ISO 178 |
| Flexural Stress | 250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 161 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 1.0 | hr | |
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 250 to 270 | °C | |
| Nozzle Temperature | 200 to 250 | °C | |
| Mold Temperature | 30.0 to 80.0 | °C | |
| Back Pressure | 5.00 to 10.0 | MPa | |
| Screw Speed | 40 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXAMID™ 236F4Q32 | SAX Polymers | Nylon 66 | SAXAMID™ |
| Spherisil C 13-08630 | SILON s.ro | PE, Unspecified | Spherisil |
| NYCOA Polyamide 5114 | Nycoa (Nylon Corporation of America) | Nylon 66 | NYCOA Polyamide |
| Latiohm 66-04 PD01 G/25-V0CT1 | LATI S.p.A. | Nylon 66 | Latiohm |
| Karina FUM\u00C9 MBATCH (SP31452) -E 27/ 8-GIN | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |