Fiberfil® J-60/30/E/HF
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Fiberfil® Engineered Plastics Inc. |
| Trademark: | Fiberfil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FeYMbY_Fiberfil-J-60-30-E-HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fiberfil®J-60/30/E/HF is a polypropylene homopolymer (PP Homopoly) material, which contains a 30% glass fiber reinforced material. This product is available in North America,. Fiberfil®The main characteristics of J-60/30/E/HF are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 0.30 | % | ASTM D955 |
| 6.35 mm | 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.030 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5860 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 89.6 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 3.5 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 5520 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 117 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 157 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 154 | °C | ASTM D648 |
| Additional Information |
|---|
| Rockwell Hardness, ASTM D785, R-Scale: 100 to 110 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUCOMP™ SAN900L | ACLO Compounders Inc. | SAN | ACCUCOMP™ |
| Dryflex® 500900S | ELASTO | SEBS | Dryflex® |
| LEXAN™ EXL1112T resin | SABIC Innovative Plastics | PC | LEXAN™ |
| OTECH PVC OE8338 - Profile | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| Braskem PE HDP0353 | Braskem IDESA | HDPE | Braskem PE |