Order Products : sales@su-jiao.com
Infino GP-5300G
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FFXf8t_Infino-GP-5300G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino GP-5300G is a Polybutylene Terephthalate (PBT) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.53 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 250°C/2.16 kg | 20 | g/10 min | ASTM D1238 |
| 250°C/2.16 kg | 22 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.90 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 6.0E-3 | % | ASTM D570 |
| Ash Content | 30 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 115 | ASTM D785 | |
| R-Scale | 118 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6800 | MPa | ASTM D638 |
| -- | 7500 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 120 | MPa | ASTM D638 |
| Yield | 141 | MPa | ISO 527-2/50 |
| Break 3 | 130 | MPa | ASTM D638 |
| Break | 141 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 3.0 | % | ASTM D638 |
| Break | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 8000 | MPa | ASTM D790 |
| -- 6 | 7900 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 190 | MPa | ASTM D790 |
| -- 8 | 199 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 85 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 79 | J/m | ASTM D256 |
| 23°C 10 | 11 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 225 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 223 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 210 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 206 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 216 | °C | ISO 306/B50 |
| -- | 220 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.70 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Desiccant Dryer | 100 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 210 to 220 | °C | |
| Middle Temperature | 225 to 230 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Nozzle Temperature | 250 | °C | |
| Mold Temperature | 60.0 to 120 | °C | |
| Injection Pressure | 24.5 to 49.0 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LL6F 801-SB | Marco Polo International, Inc. | LLDPE | MARPOL® |
| ACCUTECH™ CP0436T40L1 | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Axiall PVC 8747 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Pibiter® N400 NERO900 | SO.F.TER. SPA | PBT | Pibiter® |
| Promyde® B30 P2 GFC30 | NUREL, S.A. | Nylon 6 | Promyde® |