RTP 2102 TFE 15
| Category: | PEI , Polyether Imide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FC6Ssb_RTP-2102-TFE-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5520 | MPa | ASTM D638 |
| Tensile Strength | 110 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus | 4830 | MPa | ASTM D790 |
| Flexural Strength | 179 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (6.35 mm) | 530 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 213 | °C | |
| 1.8 MPa, Unannealed | 207 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 343 to 399 | °C | |
| Middle Temperature | 343 to 399 | °C | |
| Front Temperature | 343 to 399 | °C | |
| Mold Temperature | 93.3 to 177 | °C | |
| Injection Pressure | 103 to 138 | MPa | |
| Back Pressure | 0.345 to 0.517 | MPa | |
| Clamp Tonnage | 6.9 to 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Velocity® LCF50-PA66 | PlastiComp, Inc. | Nylon 66 | Velocity® |
| Unichem 6283MG | Colorite Polymers | PVC, Unspecified | Unichem |
| Infino NH-3208GL | SAMSUNG SDI CO., LTD. | PC | Infino |
| Jackdaw PP ER76NT6354 | Jackdaw Polymers | PP, Unspecified | Jackdaw PP |
| Jampilen RP215M | Jam Polypropylene Company | PP Random Copolymer | Jampilen |