Generic ABS+PC - Stainless Steel Fiber
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kif1Gh_Generic-ABS-PC---Stainless-Steel-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic ABS+PC - Stainless Steel Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.21 - 1.40 | g/cm³ | ASTM D792 |
| 23°C | 1.21 - 1.34 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.29 - 0.61 | % | ASTM D955 |
| 23°C | 0.30 - 0.55 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2620 - 3460 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 58.2 - 63.3 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.5 - 7.9 | % | ASTM D638 |
| Fracture, 23°C | 4.6 - 6.5 | % | ASTM D638 |
| Fracture, 23°C | 5.9 - 6.1 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2560 - 3650 | MPa | ASTM D790 |
| Flexural Strength | |||
| 23°C | 87.6 - 122 | MPa | ASTM D790 |
| 23°C | 75.0 - 86.3 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 - 84 | J/m | ASTM D256 |
| 23°C | 5.0 - 9.6 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 210 - 1100 | J/m | ASTM D256 |
| 23°C | 31 - 32 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 95.4 - 110 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 90.0 - 104 | °C | ISO 75-2/A |
| CLTE - Flow | 5.8E-5 - 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0 - 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 5.5 - 1.3E+7 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 93.3 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 227 - 280 | °C | |
| Middle Temperature | 238 - 280 | °C | |
| Front Temperature | 249 - 283 | °C | |
| Processing (Melt) Temp | 241 - 285 | °C | |
| Mold Temperature | 71.9 - 72.5 | °C | |
| Injection Pressure | 86.0 - 86.4 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic ABS+PC - Stainless Steel FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumitomo Epoxy EM 7302XLD | Sumitomo Bakelite North America, Inc. | Epoxy | Sumitomo Epoxy |
| Abstron IM11BM | Bhansali Engineering Polymers Limited | ABS | Abstron |
| ALFATER XL® A90E 1GP0000 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| ExxonMobil™ PP1352E1 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |
| OpteSTAT™ MB PETG 4000 | Ovation Polymers Inc. | PETG | OpteSTAT™ |