Riteflex® 672
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Riteflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FBbIHa_Riteflex-672.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Riteflex 672 is a 72 Shore D Hardness thermoplastic polyester elastomer with a high modulus. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.25 | g/cm³ | ASTM D792 |
| -- | 1.26 | g/cm³ | ISO 1183 |
| Specific Volume | 0.802 | cm³/g | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ross Flex | > 1.0E+6 | Cycles | Internal method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 217.2 | kN/m | ASTM D1004 |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) | |||
| -- | 10 - 15 | g/10 min | ASTM D1238 |
| -- 1 | 16 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 2.0 | % | ASTM D955 |
| Vertical flow direction | 1.7 - 2.2 | % | ISO 294-4 |
| Flow direction | 1.7 - 2.2 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shaw D | 72 | ASTM D2240 | |
| Shaw D, 15 seconds | 72 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 635 | MPa | ASTM D638 |
| -- | 500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | |||
| Yield | 28.0 | MPa | ISO 527-2/1A/50 |
| Fracture, 23°C | 29.2 | MPa | ASTM D638 |
| Fracture | 40.0 | MPa | ISO 527-2 |
| 5.0% strain | 21.0 | MPa | ISO 527-2 |
| 10% strain | 27.0 | MPa | ISO 527-2 |
| 50% strain | 25.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield | 19 | % | ISO 527-2/1A/50 |
| Fracture, 23°C | 300 | % | ASTM D638 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2/1A/50 |
| Flexural Modulus | ISO 178 | ||
| -40°C | 2400 | MPa | ISO 178 |
| 23°C | 450 | MPa | ISO 178 |
| Flexural Stress (23°C) | 22.0 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, CS-18 Wheel) | 30.0 | mg | ASTM D4060 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | |||
| -- | 214 | kN/m | ASTM D624 |
| Flow 2 | 190 | kN/m | ISO 34-1 |
| Compression Set (23°C) | < 1.0 | % | ASTM D395 |
| Bayshore Resilience | |||
| -- | 40 | % | Internal method |
| -- | 40 | % | ASTM D2632 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.5 | kJ/m² | ISO 179/1eA |
| 23°C | 19 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | ||
| -40°C | 4.8 | kJ/m² | ISO 180/1A |
| 23°C | 16 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 118 | °C | ISO 75-2/B |
| Glass Transition Temperature | -23.3 | °C | ASTM D3418 |
| Vicat Softening Temperature | 204 | °C | ASTM D1525 |
| Melting Temperature | |||
| -- 3 | 215 | °C | ISO 11357-3 |
| -- | 214 | °C | ASTM D3418 |
| CLTE - Flow | |||
| -- | 1.7E-4 | cm/cm/°C | ASTM D696 |
| -- | 1.4E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+17 | ohms | IEC 60093 |
| Dielectric Strength | 28 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.70 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.040 | IEC 60250 | |
| Comparative Tracking Index | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Max Regrind | 25 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 215 - 230 | °C | |
| Middle Temperature | 215 - 230 | °C | |
| Front Temperature | 215 - 230 | °C | |
| Nozzle Temperature | 215 - 230 | °C | |
| Processing (Melt) Temp | 220 - 235 | °C | |
| Mold Temperature | 20.0 - 55.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 - 0.345 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 220 to 235°CZone 4 Temperature: 215 to 230°CFeed Temperature: 200 to 215°C |
| Note Message | |
|---|---|
| 1 . | 2.16 kg |
| 2 . | Die C |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makropol® PC A3 MF UV RUB0032 PC322 MSP | Petropol Industry and Trade of Polymers LTDA | PC | Makropol® PC |
| Novalloy-A A5732 | PlastxWorld Inc. | ABS+Nylon | Novalloy-A |
| AVP™ ZLL12CP | SABIC Innovative Plastics | PC | AVP™ |
| Geon™ BIO RA551S | PolyOne Corporation | PVC, Flexible | Geon™ BIO |
| LUVOCOM® 19-8373 | Lehmann & Voss & Co. | Nylon 46 | LUVOCOM® |