LNP™ THERMOCOMP™ RC006 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v9VSEf_LNP-THERMOCOMP-RC006-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RC006 is a compound based on Nylon 66 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound RC-1006 Product reorder name: RC006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 | % | ASTM D955 |
| Across Flow : 24 hr | 0.60 | % | ASTM D955 |
| Across Flow : 24 hr | 0.56 | % | ISO 294-4 |
| Flow : 24 hr | 0.080 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.60 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 27800 | MPa | ASTM D638 |
| -- | 22700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 266 | MPa | ASTM D638 |
| Break | 271 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.7 | % | ASTM D638 |
| Break | 1.9 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 18800 | MPa | ASTM D790 |
| -- | 21000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 407 | MPa | ASTM D790 |
| -- | 412 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.46 | ||
| vs. Itself - Static | 0.36 | ||
| Wear Factor - Washer | 20.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 96 | J/m | ASTM D256 |
| 23°C 2 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1000 | J/m | ASTM D4812 |
| 23°C 3 | 68 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 15.0 | J | ASTM D3763 |
| -- | 3.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 262 | °C | ASTM D648 |
| CLTE | |||
| Flow : -40 to 40°C | 1.1E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 4.9E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer N93H | Precision Polymer Engineering Ltd. | NBR | Precision Polymer |
| Sindustris PE XL8081UC | Sincerity Australia Pty Ltd. | PE, Unspecified | Sindustris PE |
| TOLEN H252 IM | SIBUR, LLC | PP Homopolymer | TOLEN |
| INELEC PPSCF40 | Infinity LTL Engineered Compounds | PPS | INELEC |
| Sylvin 3290-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |