Bayblend® FR3008 HR
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Bayblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F3fDz3_Bayblend-FR3008-HR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| (PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; improved chemical and very good hydrolysis resistance; HDT/A >= 85 °C; Vicat/B 120 temperature = 103 °C; UL recognition 94 V-0 (1.5 mm); glow wire test (GWFI): 960 °C (2.0 mm); good light stability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (240°C/5.0 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 2577 | ||
| Across Flow : 240°C, 3.00 mm | 0.50 to 0.70 | % | |
| Flow : 240°C, 3.00 mm | 0.50 to 0.70 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.50 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2700 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 60.0 | MPa | |
| Break, 23°C | 50.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 4.0 | % | |
| Break, 23°C | > 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 10 | kJ/m² | |
| 23°C | 30 | kJ/m² | |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 85.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 101 | °C | ISO 306/B50 |
| -- | 103 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 7.6E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 8.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.20 | ||
| 23°C, 1 MHz | 3.10 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 5.0E-3 | ||
| 23°C, 1 MHz | 7.0E-3 | ||
| Comparative Tracking Index (Solution A) | 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.00 mm | 5VB | ||
| 3.00 mm | 5VA |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity 2(260°C) | 195 | Pa·s | ISO 11443-A |
| Note Message | |
|---|---|
| 1 . | 150x105x3 mm, 80°C MT |
| 2 . | 1000/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® D6870 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Altuglas® VM 100 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| BRALEN® FB 08-64 | Slovnaft Petrochemicals, s.r.o. | LDPE | BRALEN® |
| Elastron® V V101.A79.N | Elastron USA, Inc. | TPV | Elastron® V |
| Lupol® HI5204H | LG Chem Ltd. | TPO | Lupol® |