Lucalen A2920M Q225
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Lucalen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F1dW5O_Lucalen-A2920M-Q225.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lucalen A 2920 M Q225 is an additivated, low density polyethylene, containing comonomer. It is delivered in pellet form. Additional Customer Applications: Adhesive layer Foodlaw compliance information about this product can be found in separate product documentation. This product is not intended for use in medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.927 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 38 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 90.0 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 6.00 | MPa | ISO 527-2 |
| Coefficient of Friction | > 0.80 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 40 to 100 µm | ||
| Dart Drop Impact (50 µm, Blown Film) | 650 | g | ASTM D1709 |
| Water Vapor Transmission Rate (38°C, 90% RH, 100 µm) | 2.3 | g/m²/24 hr | ISO 2556 |
| Oxygen Permeability (23°C, 100.0 µm) | 2400 | cm³/m²/bar/24 hr | ISO 2556 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comonomer AA | 4.0 | % | DIN 51451 |
| Comonomer BA | 7.0 | % | DIN 51451 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 74.0 | °C | ISO 306/A50 |
| Melting Temperature | 96.0 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.0 µm) | > 80 | ASTM D2457 | |
| Haze (50.0 µm) | < 6.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 140 to 180 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MEGOLON™ S340 | AlphaGary | TP, Unspecified | MEGOLON™ |
| Wellamid® 22LHI4 XE-GY1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| ALTECH® PC A 1000/227 UV | ALBIS PLASTIC GmbH | PC | ALTECH® PC |
| EVICOM™ PT 80/5 | INEOS Compounds | PVC, Flexible | EVICOM™ |
| Elastron® G G101.A73.N | Elastron USA, Inc. | SEBS | Elastron® G |