INEOS LDPE M21E730
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F0lTyM_INEOS-LDPE-M21E730.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LDPE ionomer for film products Benefits & Features M21E730 is an ionomer, produced by the neutralization of an ethylene methacrylic acid (MAA) copolymer. It offers the following properties:
Applications M21E730 has been developed for easy tear film applications such as collation shrink film, envelopes, overwrap and bags. It can be blended or co-extruded with other types of polyethylene to tailor performance. We recommend that you consult your INEOS technical representative for further advice on the use of M21E730. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.933 | g/cm³ | ISO 1872, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ISO 1133 |
| Methacrylic Acid Content | 1.7 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 1184 | ||
| 1% secant, MD : 50 µm, blown film | 165 | MPa | ISO 1184 |
| 1% secant, TD : 50 µm, blown film | 175 | MPa | ISO 1184 |
| Tensile Stress | ISO 1184 | ||
| MD : Yield, 50 µm, blown film | 11.0 | MPa | ISO 1184 |
| TD : Yield, 50 µm, blown film | 10.0 | MPa | ISO 1184 |
| MD : 50 µm, blown film | 28.0 | MPa | ISO 1184 |
| TD : 50 µm, blown film | 29.0 | MPa | ISO 1184 |
| Tensile Elongation | ISO 1184 | ||
| MD : Broken, 50 µm, blown film | 200 | % | ISO 1184 |
| TD : Broken, 50 µm, blown film | 400 | % | ISO 1184 |
| Dart Drop Impact (50 µm, Blown Film) | 750 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 48 | g | ASTM D1922 |
| TD : 50 µm, blown film | 54 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 92.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 60 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 9.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Values determined on a 50 µm film, 2.5:1 blow-up ratio, 180°C melt temperature |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stanyl® TW271B6 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| Ferro PP TPP20AN75BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| LNP™ STAT-KON™ PE002 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ STAT-KON™ |
| LUVOCOM® 1-7701 VP | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| ESTOPLAST ZK 6415BB01 | Ester Industries Ltd. | PC | ESTOPLAST ZK |