Versaflex™ CL E95
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Versaflex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EvhlDP_Versaflex-CL-E95.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Versaflex™CL E9 is a material with extremely high transparency, high performance and high temperature heating. It is an ideal material for medical and food packaging. Versaflex™CL E9 also did not use plasticizers. New Products. Commercial norms have not yet been established. • Flexible • Special formula without plasticizer • High transparency |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 95 | ASTM D2240 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability (21°C, 120 µm) | 150 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Oxygen Transmission Rate (21°C, 120 µm) | 1200 | cm³/m²/24 hr | ASTM D3985 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% strain, 23°C 2 | 11.6 | MPa | ASTM D412 |
| 300% strain, 23°C 3 | 11.9 | MPa | ASTM D412 |
| Tensile Strength (Break, 23°C) | 17.2 | MPa | ASTM D412 |
| Tensile Elongation (Break, 23°C) | 580 | % | ASTM D412 |
| Tear Strength | 126 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 22°C, 22 hr | 38 | % | ASTM D395B |
| 70°C, 22 hr | 66 | % | ASTM D395B |
| 100°C, 22 hr | 71 | % | ASTM D395B |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity | ASTM D3835 | ||
| 200°C, 1340 sec^-1 | 138 | Pa·s | ASTM D3835 |
| 200°C, 11200 sec^-1 | 30.0 | Pa·s | ASTM D3835 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 204 | °C | |
| Die Temperature | 171 - 199 | °C |
| Extrusion instructions |
|---|
| Color concentrates with polypropylene (PP), ethylene vinyl acetate (EVA), or low density polyethylene (PE) carriers are most suitable for coloring Versaflex™ CL E95. Improved color dispersion can be achieved by using higher melt flow concentrates (with a melt flow from 25 - 40g/10 min). Typical loadings for color concentrates are 1% to 5% by weight. Liquid color can be used, but mineral oil based carriers may have a significant effect on the final hardness value. Concentrates based on PVC should not be used. A high color match consistency can be obtained by using precolored compounds available from GLS. The final determination of color concentrate suitability should be determined by customer trials.Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).Drying is not Required.Rear Zone = 330-370FCenter Zone = 350-400FFront Zone = 360-420FScrew Speed = 100-500 RPM |
| Note Message | |
|---|---|
| 1 . | 2 hours |
| 2 . | Mouth die c |
| 3 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 31T1010 resin | SABIC Innovative Plastics | PP, Unspecified | SABIC® PPcompound |
| NANCAR® 3245C | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| ACCUTECH™ CP0436T10L1 | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Desmovit® DP R 9929 | geba Kunststoffcompounds GmbH | TPU-Ester/Ether | Desmovit® |
| Lupox® TE5000GH | LG Chem Ltd. | PC+PBT | Lupox® |