Taitalac® 3100
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Taita Chemical Company, Ltd. |
| Trademark: | Taitalac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ett2PB_Taitalac-3100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Taitalac®3100 is an acrylonitrile butadiene styrene (ABS) material,. This product is available in North America or Asia Pacific region. The processing method is injection molding. Taitalac®The main features of the 3100 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 0.80 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | < 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | < 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield, 23°C, 3.18mm | 32.4 | MPa | ASTM D638 |
| Fracture, 23°C, 3.18mm | 27.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, 3.18 mm) | 90 | % | ASTM D638 |
| Flexural Modulus 3(23°C) | 2000 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 23°C) | 58.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.18 mm | 490 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 450 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 85.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 102 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 200 - 230 | °C | |
| Middle Temperature | 210 - 240 | °C | |
| Front Temperature | 200 - 230 | °C | |
| Nozzle Temperature | 220 - 240 | °C | |
| Processing (Melt) Temp | 185 - 195 | °C | |
| Mold Temperature | 40.0 - 70.0 | °C | |
| Injection Pressure | 0.345 - 0.483 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 30 - 100 | rpm |
| Injection instructions |
|---|
| Injection Pressure: Moderately High to High |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADDILENE J 290 M20 F | ADDIPLAST | PP, Unspecified | ADDILENE |
| AMTOPP AF40 | Inteplast Group | PP, Unspecified | AMTOPP |
| APEX® 85-J438-D | Teknor Apex Company | PVC, Flexible | APEX® |
| Fainplast PVC GSK 73/N-UV | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Sylvin 2900-78 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |