Order Products : sales@su-jiao.com
Starex GR-4020L
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3XUrhY_Starex-GR-4020L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS/GF material that is applied to printer LBP fuser |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.18 | g/cm³ | ASTM D792 |
| -- | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 220°C/10.0 kg | 7.0 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 9.0 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 to 0.30 | % | ASTM D955 |
| Ash Content | 20 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5300 | MPa | ASTM D638 |
| -- | 5600 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 88.0 | MPa | ASTM D638 |
| Yield | 88.0 | MPa | ISO 527-2/50 |
| Break 3 | 86.0 | MPa | ASTM D638 |
| Break | 88.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 2.5 | % | ASTM D638 |
| Break | 2.5 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 5300 | MPa | ASTM D790 |
| -- | 6400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 6 | 110 | MPa | ASTM D790 |
| -- | 125 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7(23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 67 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 68 | J/m | ASTM D256 |
| 23°C 8 | 7.9 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 104 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 103 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 100 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 97.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 103 | °C | ISO 306/B50 |
| -- | 106 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| 6.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 180 to 190 | °C | |
| Middle Temperature | 200 to 210 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Nozzle Temperature | 240 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.8 mm/min |
| 7 . | Thickness: 4 mm |
| 8 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nanjing Hongrui PC CT302 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PC Alloy | Nanjing Hongrui PC |
| NYCOA Polyamide GR30 V0 Black | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| Bluestar Epoxy E-52D | Bluestar New Chemical Materials Co. Ltd | Epoxy | Bluestar Epoxy |
| LubriOne™ LB 6000-5006 NHFR NATURAL | PolyOne Corporation | Nylon 6 | LubriOne™ |
| LNP™ LUBRILOY™ RF208 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |