Nylene® 7228 HS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Custom Resins Group |
| Trademark: | Nylene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Eiyl1z_Nylene-7228-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Nylene® 7228 HS is a Polyamide 6 (Nylon 6) material filled with 28% glass\mineral. It is available in North America for extrusion or injection molding. Important attributes of Nylene® 7228 HS are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 66.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 8.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 3390 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 151 | °C | ASTM D648 |
| Melting Temperature | 216 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 to 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Shot Size | 25 to 75 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 249 to 277 | °C | |
| Middle Temperature | 260 to 288 | °C | |
| Front Temperature | 271 to 299 | °C | |
| Nozzle Temperature | 271 to 299 | °C | |
| Processing (Melt) Temp | 271 to 299 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Injection Pressure | 55.2 to 124 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 41.4 to 103 | MPa | |
| Back Pressure | 0.00 to 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROPRENE® 1 A85 M1N | Taro Plast S.p.A. | TPV | TAROPRENE® |
| WELLAMID Nylon 6600 PA-66-HWV0CP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| CALP 1470G-2 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| LNP™ STAT-KON™ AX02747 compound | SABIC Innovative Plastics | ABS | LNP™ STAT-KON™ |
| CYCOLAC™ FXS610SK resin | SABIC Innovative Plastics Europe | ABS | CYCOLAC™ |