Beetle® PET1610F
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Beetle® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EZygCQ_Beetle-PET1610F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PET1610F is a reinforced PET containing 50% glass fiber, which has good mechanical properties and excellent mold release at high temperature. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.74 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.30 - 0.90 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 19000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 160 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 17500 | MPa | ISO 178 |
| Flexural Stress | 260 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 13 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 40 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 220 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.00 mm) | 10 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.57 mm) | HB | UL 94 | |
| Oxygen Index | 21 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 275 - 290 | °C | |
| Middle Temperature | 275 - 290 | °C | |
| Front Temperature | 275 - 290 | °C | |
| Processing (Melt) Temp | < 290 | °C | |
| Mold Temperature | 120 - 140 | °C | |
| Injection Rate | Fast | ||
| Screw Speed | 50 - 100 | rpm |
| Injection instructions |
|---|
| 背压：低注射压力：高 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAYPRENE® NB221-S4085 | R&P (Pte.) Ltd. | TPE | RAYPRENE® |
| Nanjing Hongrui PP P830 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PP, Unspecified | Nanjing Hongrui PP |
| ALCOM® PC 740/4 UV WT1240-10LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| apinat® A 65 | API SpA | TPE | apinat® |
| Trilliant™ HC 5210-0003 Black | PolyOne Corporation | PP Random Copolymer | Trilliant™ HC |