Petrotene® PP A3 T20 HF NTLA010 PH370
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Petrotene® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yBPGYD_Petrotene-PP-A3-T20-HF-NTLA010-PH370.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene of high flow natural 20% mineral reinforced for injection molding, resistant to oil, grease and many solvents, good set of mechanical properties and good dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 to 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 23 to 27 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.90 to 1.2 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.020 | % | ASTM D570 |
| Ash Content | 18 to 22 | % | ASTM D2584 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 30.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 2700 | MPa | ASTM D790 |
| Flexural Strength | 45.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 68.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 140 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 40 | kV/mm | ASTM D149 |
| Dissipation Factor (1 kHz) | 2.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen D50G | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| Haysite BMC 270FRII | Haysite Reinforced Plastics | Polyester, TS | Haysite BMC |
| Lytex 9063NWC | Quantum Composites Inc. | Epoxy | Lytex |
| POLYFLON™ F-205 | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |
| TECACOMP® PA66 GF25 TF10 HI natural 9173 | Ensinger GmbH | Nylon 66 | TECACOMP® |