Hostalen CRP 100 RESIST CR W blue
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostalen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EXdqgt_Hostalen-CRP-100-RESIST-CR-W-blue.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostalen CRP 100 RESIST CR W blue is a high density polyethylene (HDPE), dark blue coloured similar RAL 5005 with high melt viscosity for extrusion, injection and compression moulding. The product is classified as PE 100-RC and provides a very good long term hydrostatic strength. Especially developed for non-conventional pipe installations methods the product has a superior resistance to slow crack growth. It fulfils the material requirements of PAS 1075:2009-04. It is not intended for medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 7.3 | g/10 min | |
| 190°C/5.0 kg | 0.27 | g/10 min | |
| FNCT - 4.0 MPa (80°C) 1 | > 1 | yr | ISO 16770 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Creep Modulus 2 | DIN 19537-2 | ||
| 1 min | 1.10 | GPa | |
| 2000 hr | 0.330 | GPa | |
| 24 hr | 0.560 | GPa |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (210°C) | 30 | min | ISO 11357-6 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MRS Classification | 10.0 | MPa | ISO TR 9080 |
| Odor Threshold | < 2.00 | EN 1622/EN 1420 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 3 sec) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant (23°C) | 1050 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 23.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield, 23°C | 9.0 | % | ISO 527-2/50 |
| Break | > 350 | % | EN 638 |
| Tensile Creep Modulus 3 | ISO 899-1 | ||
| 1 hr | 850 | MPa | |
| 1000 hr | 360 | MPa | |
| Flexural Stress (3.5% Strain) | 21.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 26 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 74.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 to 280 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 2% Arkopal N 100 |
| 2 . | 4 point loading method |
| 3 . | 2.0 MPa load |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fluoroplex CG 25 - GMP | UNIFLON | PTFE | Fluoroplex |
| Hangzhou Plastic Pharma Grade PVC Rigid Film | Hangzhou Plastic Industry Co., Ltd. | Film, PVC | Hangzhou Plastic |
| ESPRENE EPDM 400 | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |
| Leona™ 90G33 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| POLYabs T00 | Polykemi AB | ABS | POLYabs |