RTP 2800 B-45A HF
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6SZaCx_RTP-2800-B-45A-HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Flow |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792 |
| Moisture Content | < 0.040 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 45 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(100% Strain, 3.18 mm) | 1.24 | MPa | ASTM D412 |
| Tensile Strength 2(Yield, 3.20 mm) | 3.31 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 450 | % | ASTM D412 |
| Tear Strength 4 | 13.1 | kN/m | ASTM D624 |
| Compression Set 5 | ASTM D395B | ||
| 23°C, 22 hr | 12 | % | |
| 70°C, 22 hr | 28 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Dew Point | -17.8 | °C | |
| Processing (Melt) Temp | 182 to 210 | °C | |
| Mold Temperature | 15.6 to 65.6 | °C |
| Note Message | |
|---|---|
| 1 . | Die C, 510 mm/min |
| 2 . | Die C, 500 mm/min |
| 3 . | Die C, 500 mm/min |
| 4 . | Die C |
| 5 . | Type 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BESTNYL SE15VI02AS16 | Triesa Plastics | Nylon 66 | BESTNYL |
| FILLMA 5002F30A | POLYROCKS CHEMICAL CO., LTD | PP, Unspecified | FILLMA |
| Kumho EP HAG 5220FR | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho EP |
| Karina SILVER COLOR CONCENTRATE 47/9-FC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ UFW49RSC compound | SABIC Innovative Plastics Europe | PPA | LNP™ THERMOCOMP™ |