LEXAN™ 3412ECR resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EThaqg_LEXAN-3412ECR-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEXAN 3412ECR Polycarbonate (PC) resin is a 20% glass fiber filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant GF-PC has an UL-94 V0 rating and is available in various opaque color options. LEXAN 3412ECR is a resin designed to meet the needs of high stiffness applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.30 | g/cm³ | ASTM D792 |
| -- | 1.36 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 7.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 7.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.20 to 0.50 | % | |
| Across Flow : 3.20 mm | 0.20 to 0.50 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.29 | % | |
| Equilibrium, 23°C, 50% RH | 0.12 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5500 | MPa | ASTM D638 |
| -- | 6000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 90.0 | MPa | ASTM D638 |
| Yield | 95.0 | MPa | ISO 527-2/5 |
| Break 3 | 87.0 | MPa | ASTM D638 |
| Break | 90.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.1 | % | ASTM D638 |
| Yield | 2.8 | % | ISO 527-2/5 |
| Break | 3.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 5000 | MPa | ASTM D790 |
| -- 6 | 5500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 140 | MPa | ISO 178 |
| Yield, 50.0 mm Span 7 | 156 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 8 | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength 9 | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 40 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 110 | J/m | ASTM D256 |
| 23°C | 110 | J/m | ASTM D256 |
| -30°C 10 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 12 | ISO 180/1U | ||
| -30°C | 35 | kJ/m² | |
| 23°C | 35 | kJ/m² | |
| Instrumented Dart Impact (23°C, Total Energy) | 20.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 64.0 mm Span 13 | 141 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 141 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 14 | 136 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 147 | °C | ASTM D1525 15 |
| -- | 145 | °C | ISO 306/B50 |
| -- | 146 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 40°C | 3.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 80°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 3.30 | ||
| 60 Hz | 3.30 | ||
| 1 MHz | 3.30 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 0.020 | ||
| 60 Hz | 0.020 | ||
| 1 MHz | 0.010 | ||
| Arc Resistance 16 | PLC 7 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | 5VA | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 825 | °C | IEC 60695-2-13 |
| Oxygen Index | 40 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 266 to 288 | °C | |
| Middle Temperature | 277 to 299 | °C | |
| Front Temperature | 288 to 310 | °C | |
| Nozzle Temperature | 282 to 304 | °C | |
| Processing (Melt) Temp | 288 to 310 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*3 sp=62mm |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 |
| 11 . | 80*10*3 |
| 12 . | 80*10*3 |
| 13 . | 80*10*4 mm |
| 14 . | 80*10*4 mm |
| 15 . | Rate B (120°C/h), Loading 2 (50 N) |
| 16 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nylene® NX4004A HS BLACK | Custom Resins Group | Nylon 6 | Nylene® |
| AXELERON™ CS 6005 NT CPD | The Dow Chemical Company | LDPE | AXELERON™ |
| DJSilicone NE-G160 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Sylvin 8205-75UV Grey 9625 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Moplen EP440G | LyondellBasell Industries | PP, HMS | Moplen |