Order Products : sales@su-jiao.com
Tarnoform® 500 LS
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Grupa Azoty S.A. |
| Trademark: | Tarnoform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EELypl_Tarnoform-500-LS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Tarnoform® 500 LS is the very easy flowing, fast cycling injection-moulding grade, good chemical resistance, modified with soluble light stabilisers improving light resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 27 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 23.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (2.00 mm) | 2.0 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.80 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 160 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 63.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 8.0 | % | |
| Break | 20 | % | |
| Flexural Modulus 1 | 2550 | MPa | ISO 178 |
| Flexural Stress 2 | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -- | 5.5 | kJ/m² | |
| -30°C | 4.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -- | 140 | kJ/m² | |
| -30°C | 110 | kJ/m² | |
| Notched Izod Impact Strength | 5.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 115 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/B |
| Melting Temperature | 167 | °C | ISO 11357-3 |
| CLTE - Flow (23 to 55°C) | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Limit of Temperature - a few hours operation | 100 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Type | POM-K, M-GNL, 05-002 | ISO 1874 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 25 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 Hz) | 3.90 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 180 to 230 | °C | |
| Mold Temperature | 60.0 to 120 | °C | |
| Injection Pressure | 60.0 to 120 | MPa | |
| Injection Rate | Slow-Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VENYL UG400 | AD majoris | Nylon 66 | VENYL |
| AKROMID® A3 GK 30 natural (3689) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Argothane® 18214 | Argotec LLC | TPU, Unspecified | Argothane® |
| COSMOPLENE® FY4012E | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Homopolymer | COSMOPLENE® |
| Esterlloy™ AT11N | Asahi Kasei Chemicals Corporation | ABS Alloy | Esterlloy™ |