Mecoline IS RDX 5240 F
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Melos GmbH |
| Trademark: | Mecoline |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E9Vref_Mecoline-IS-RDX-5240-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Appliance wire, wire for solar panels, gearboxes, etc. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 4.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | IEC 811-1-1 | ||
| -- 1 | 16.0 | MPa | |
| -- 2 | > 10.0 | MPa | |
| Tensile Strain | |||
| Break 3 | 350 | % | IEC 811-1-1 |
| Break 4 | > 500 | % | IEC 811-1-1 |
| Break, -50°C | > 30 | % | IEC 811-1-4 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (158°C, 168 hr) | 3.0 | % | IEC 811-1-2 |
| Change in Tensile Strain at Break in Air (158°C, 168 hr) | -4.0 | % | IEC 811-1-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deformation (158°C) | 12 | % | |
| Hot Set 5 | IEC 540 | ||
| Elongation under load | < 40 | % | |
| Residual elongation | < 10 | % |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 155 to 165 | °C | |
| Extruder Screw L/D Ratio | >24.0:1.0 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Electric Strength | 20 | kV/mm | IEC 60243-1 |
| Dielectric Constant (50 Hz) | 3.50 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 32 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 130 to 140 | °C | |
| Cylinder Zone 2 Temp. | 140 to 150 | °C | |
| Cylinder Zone 3 Temp. | 150 to 160 | °C | |
| Cylinder Zone 4 Temp. | 155 to 165 | °C | |
| Cylinder Zone 5 Temp. | 155 to 165 | °C | |
| Adapter Temperature | 155 to 165 | °C | |
| Die Temperature | 160 to 170 | °C |
| Note Message | |
|---|---|
| 1 . | After crosslinking |
| 2 . | Before crosslinking |
| 3 . | After crosslinking |
| 4 . | Before crosslinking |
| 5 . | at 200°C/15min/0.2 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® Fine Powders T NAT BHV RX 2 | Arkema | Nylon 11 | Rilsan® Fine Powders |
| SABIC® HDPE M30053S | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| Sinvicomp SRP2009M | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Sylvin 2900-45 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ STAT-KON™ EE003XXC compound | SABIC Innovative Plastics | PEI | LNP™ STAT-KON™ |