DINALEN® 50

Category:	LDPE , Low Density Polyethylene
Manufacturer:	DIOKI d.d.
Trademark:	DINALEN®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	E2bqdV_DINALEN-50.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

DINALEN 50 is low density polyethylene containing no additives. It is primarily intended for blow and cast film extrusion while other processing techniques can be used to a lesser extent.

DINALEN 50 exhibits very good draw-down with good balance of stiffness, mechanical and optical properties of extruded film.

DINALEN 50 is extruded at recommended melt temperature range between 160°C and 180° C. Recommended film thickness: 0.025 to 0.060 mm.

Application

Thin non-slippery film of high gloss and transparency

Heat shrinkable film with excellent stiffness for industrial bundling

Extruded foams with physical blowing agent

Small diameter pipe extrusion

Wire and cable sheathing

Injection moulded thick-walled products

Blown packaging and other shallow objects

Mixing and co-extrusion with suitable polyolefin grades

General Information
Features	Good Drawdown Good Heat Shrinkability Good Stiffness High Clarity High Gloss Opticals
Uses	Blending Cast Film Film Foam Packaging Piping Shrink Wrap
Agency Ratings	EC 1907/2006 (REACH) EU 2002/72/EC EU 2004/1/EC EU 2004/19/EC EU 2005/79/EC EU 2007/19/EC EU 2008/39/EC EU 94/62/EC
RoHS Compliance	RoHS Compliant
Appearance	Clear/Transparent
Forms	Pellets
Processing Method	Blown Film Cast Film Coextrusion Foam Extrusion Injection Molding Pipe Extrusion Wire & Cable Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.923	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	2.0	g/10 min	ISO 1133

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D)	45		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (Compression Molded)	200	MPa	ISO 527-2
Tensile Stress			ISO 527-2
Yield, Compression Molded	11.0	MPa
Break, Compression Molded	15.0	MPa
Tensile Strain (Break, Compression Molded)	620	%	ISO 527-2
Coefficient of Friction			ISO 8295
vs. Itself - Dynamic	> 0.40
vs. Itself - Static	> 0.40

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	50	µm
Film Thickness - Recommended / Available	0.025mm to 0.060 mm
Tensile Strength			ISO 527-3
MD : 50 µm	20.0	MPa
TD : 50 µm	17.0	MPa
Tensile Elongation			ISO 527-3
MD : Break, 50 µm	220	%
TD : Break, 50 µm	330	%
Dart Drop Impact ¹(50 µm)	220	g	ISO 7765-1
Trouser Tear Resistance			ISO 6383-1
MD : 50 µm	90.0	N/mm
TD : 50 µm	80.0	N/mm

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	94.0	°C	ISO 306/A50
Melting Temperature	113	°C	ISO 11357-3

Optical	Nominal Value		Test Method
Gloss			ASTM D2457
20°, 50.0 µm	> 60
60°, 50.0 µm	> 110

Extrusion	Nominal Value	Unit
Melt Temperature	160 to 180	°C

Note Message
1 .	Profile 2

Resin Grade	Manufacturer	Category	Trademark
Retpol® 1085 HS 70104	PolyPacific Pty. Ltd.	PP Homopolymer	Retpol®
Sylvin 916VO-95 Black	Sylvin Technologies Incorporated	PVC, Flexible	Sylvin
Axiall PVC 3801	Axiall Corporation	PVC, Rigid	Axiall PVC
Jiangsu Sinarise JM8911	Jiangsu Sinarise New Material Technology Co., Ltd	TPE	Jiangsu Sinarise
LITEN BB 38 S	UNIPETROL RPA	PE Copolymer	LITEN