FREQTIS® P0833A
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Polyplastics Co., Ltd. |
| Trademark: | FREQTIS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DunspT_FREQTIS-P0833A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FREQTIS® P0833A is a Polyphenylene Sulfide (PPS) product filled with 60% mineral. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| UL File Number |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.12 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | |||
| Across Flow : 2.00 mm | 0.60 | % | |
| Flow : 2.00 mm | 0.30 | % | |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 115 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.80 | % | ISO 527-2 |
| Flexural Modulus | 18000 | MPa | ISO 178 |
| Flexural Stress | 165 | MPa | ISO 178 |
| Flexural Strain | 0.90 | % | ISO 178 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color Number | KD3051 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.3 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE | |||
| Flow | 2.0E-5 | cm/cm/°C | |
| Transverse | 3.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (3.00 mm) | 12 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 1 MHz | 8.00 | ||
| 3.00 GHz 2 | 8.00 | ||
| Dissipation Factor 3(3.00 GHz) | 3.0E-3 | ||
| Arc Resistance | 159 | sec | |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (310°C, 1000 sec^-1) | 290 | Pa·s | ISO 11443 |
| Note Message | |
|---|---|
| 1 . | 80x80x2 mm |
| 2 . | Cavity Resonator Method |
| 3 . | Cavity Resonator Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoFlo 30A-300 | KMI Group Inc. | SEBS | PrimoFlo |
| Formolene® 5143S | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| Hostacom DYS 707N HS Natural | LyondellBasell Industries | TPO (POE) | Hostacom |
| Kumho SBR 1789 | Korea Kumho Petrochemical Co., Ltd. | SBR, Emulsion | Kumho SBR |
| VALOX™ 830 resin | SABIC Innovative Plastics | PBT | VALOX™ |