SABIC® PPcompound 2401-1
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NV1BCq_SABIC-PPcompound-2401-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A grade which offers excellent acoustic insulation properties, specially developed for wheel well cladding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 7.0 | g/10 min | ISO 1133 |
| 230°C/5.0 kg | 30 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 50 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20mm | 11.0 | MPa | ISO 527-2/5/50 |
| Fracture, 3.20mm | 12.0 | MPa | ISO 527-2/5/50 |
| Tensile Strain (Break, 3.20 mm) | 500 | % | ISO 527-2/5/50 |
| Flexural Modulus 1 | 600 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | No Break | ISO 179 | |
| Charpy Unnotched Impact Strength (-40°C) | No Break | ISO 179 | |
| Notched Izod Impact | ISO 180/3A | ||
| -40°C | 5.0 | kJ/m² | ISO 180/3A |
| -20°C | 15 | kJ/m² | ISO 180/3A |
| 0°C | No Break | ISO 180/3A | |
| 23°C | No Break | ISO 180/3A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 60.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 105 | °C | ISO 306/A50 |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| Mold Shrinkage, SABIC Method: 1.1% |
| Note Message | |
|---|---|
| 1 . | Method I (three-point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Somos® 9420 | DSM Somos® | Unspecified | Somos® |
| Bapolene® LD200B | Bamberger Polymers, Inc. | LDPE | Bapolene® |
| Fainplast PVC GK 89/R | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Ekatal® C 9 X | Sattler KunststoffWerk GmbH | Acetal (POM) Copolymer | Ekatal® |
| KRALEX® 1783 | Synthos S.A. | SBR, Emulsion | KRALEX® |