Kingplate™ H2938-P
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | Kingplate™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Dl0gf7_Kingplate-H2938-P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABSH2938-P is a medium heat resistance ABS resion for plating , offering high rigidity and high impact. |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 9.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.40 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 37.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 63 | % | ISO 527-2/50 |
| Flexural Modulus 1(64.0 mm) | 2130 | MPa | ISO 178 |
| Flexural Stress 2(64.0 mm) | 60.0 | MPa | ISO 178 |
| Poisson's Ratio | 0.39 | ISO 527 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179 | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 26 | kJ/m² | |
| Charpy Unnotched Impact Strength 4 | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength 5 | ISO 180 | ||
| -30°C | 11 | kJ/m² | |
| 23°C | 24 | kJ/m² | |
| Unnotched Izod Impact Strength 6 | ISO 180 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, Unannealed | 99.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 86.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 106 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.7E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.6E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 220 to 240 | °C | |
| Front Temperature | 235 to 255 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Condition: 4 J |
| 4 . | Condition: 4 J |
| 5 . | Condition: 5.5 J |
| 6 . | Condition: 5.5 J |
| 7 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TITANLENE® LDF 200YY | Lotte Chemical Titan (M) Sdn. Bhd. | LDPE | TITANLENE® |
| Karina CLEAR PVC COMPOUND -E 80/214-SD-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Panlite® BS-8110R | TEIJIN LIMITED | PC | Panlite® |
| Polifil® PE RP-LDPE | The Plastics Group | LDPE | Polifil® PE |
| ALTECH® PA6 A 3230/100 GF10 GB20 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |