Starex SR-0305
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DZtAo2_Starex-SR-0305.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex SR-0305 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 15 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.20 mm | 0.60 | % | |
| Across Flow : 3.20 mm | 0.60 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.050 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.050 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 109 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 1 | 45.0 | MPa | ASTM D638 |
| Yield | 45.0 | MPa | ISO 527-2/50 |
| Break | 33.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 2 | 15 | % | ASTM D638 |
| Break | 15 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 3 | 2300 | MPa | ASTM D790 |
| -- 4 | 2500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 5 | 64.0 | MPa | ASTM D790 |
| -- 6 | 72.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7(23°C) | 20 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 240 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 230 | J/m | ASTM D256 |
| 23°C 8 | 23 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 85.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 85.0 | °C | |
| Vicat Softening Temperature | 100 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 160 to 180 | °C | |
| Middle Temperature | 190 to 200 | °C | |
| Front Temperature | 210 to 220 | °C | |
| Nozzle Temperature | 230 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 49.0 to 147 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Thickness: 4 mm |
| 8 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYVIN® PVC 5819ND | A. Schulman Inc. | PVC, Unspecified | POLYVIN® |
| Axiall PVC 8923 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| FLEXAREN® 14010 | Innospec Leuna GmbH | EVA | FLEXAREN® |
| Hostalen PP H2250 36 | LyondellBasell Industries | PP Homopolymer | Hostalen PP |
| Karina IVORY PVC COMP. -E 850-35/ 1-C | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |