Wellamid® MRB40K004-WT1
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Wellman Engineering Resins |
| Trademark: | Wellamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DVmi96_Wellamid-MRB40K004-WT1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Wellamid® MRB40K004-WT1 is a Polyamide 66 (Nylon 66) material filled with 40% mineral. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Typical application of Wellamid® MRB40K004-WT1: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 1.3 to 1.7 | % | |
| Flow : 23°C | 1.1 to 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 4.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 6000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 4.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 135 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 277 to 310 | °C | |
| Middle Temperature | 271 to 304 | °C | |
| Front Temperature | 266 to 299 | °C | |
| Nozzle Temperature | 254 to 293 | °C | |
| Processing (Melt) Temp | 271 to 304 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Injection Pressure | 34.5 to 138 | MPa | |
| Back Pressure | 0.345 | MPa | |
| Screw Speed | 30 to 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIBOCOMP® PEEK CF30 TS0 | EPIC Polymers | PEEK | TRIBOCOMP® |
| API PS 370-21 | American Polymers, Inc. | PS (GPPS) | API PS |
| Kepital® FC2010DX | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| Huafon JF-P-513 / JF-I-613 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Karina CLEAR PVC COMPOUND -E 75/161-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |