NuSil MED-2045
| Category: | Rubber , Rubber |
| Manufacturer: | NuSil Technology |
| Trademark: | NuSil |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DGl7vO_NuSil-MED-2045.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NuSil Technology's restricted materials may be considered for use in short-term implant applications, 29 days or less, or for external applications. High consistency rubber, or HCR, consists of high molecular weight polymer combined with silica to produce a material that can be molded, extruded, or calendared into a useful end product. An HCR has the consistency of clay and is primarily formulated in a one or two part system (peroxide and platinum catalysts respectively). Most platinum cure high consistency rubbers are two component systems with an easy-to-work-with 1:1 mix ratio. Comments: MIX RATIO 100 (A): 0.7 (B): 0.16 (C) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength (200% Strain) | 1.38 | MPa |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part C | Mixing ratio by weight: 0.16 | ||
| Component a | Mixing ratio by weight: 100 | ||
| Component B | Mixing ratio by weight: 0.70 | ||
| Post Cure Time (148°C) | 2.0 | hr |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Cure System | Platinum | ||
| Plasticity: 95 mils |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density | 1.13 | g/cm³ | |
| Curing Time (171°C) | 0.17 | hr |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore A) | 40 | ||
| Tensile Strength | 10.5 | MPa | |
| Tensile Elongation at Break | 800 | % | |
| Tear Strength | 35.0 | kN/m |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® RP 3501-C | Plastic Solutions, Inc. | PP Random Copolymer | PrimaFlex® |
| DOMAMID® 6Y10 | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| EPO-TEK® 320-LV | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| INNOPOL® PP CS 2-3522 TO BU | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |
| Extir® VERDI PD VM A2000 AE | Versalis S.p.A. | PS (EPS) | Extir® |