ACRYLITE® LED 8N LD96
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Evonik Cyro LLC |
| Trademark: | ACRYLITE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D5m7rE_ACRYLITE-LED-8N-LD96.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ACRYLITE® LED 8N LD96 Acrylic Molding Compound is a highly transparent light guide material based on ACRYLITE® 8N. In addition to the typical properties of ACRYLITE®, such as
ACRYLITE® LED 8N LD96 is developed for edge lit LED applications. The light scattering properties convert the light guide to a full illuminated panel. Furthermore, the material allows for a competely transparent view through the light guide when it is not illuminated. This opens a new degree of freedom for designers. ACRYLITE® 8N LD12 is recommended for panels with a distance of 48 cm to 96 cm between two light injecting LED strips. Application: Injection molding or extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Apparent Density | 0.66 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 3.3 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Water Absorption (Equilibrium) | < 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3240 | MPa | ASTM D638 |
| Tensile Strength | 77.9 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 4.0 to 6.0 | % | |
| Break | 4.0 to 6.0 | % | |
| Flexural Modulus | 3450 | MPa | ASTM D790 |
| Flexural Strength | 112 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm) | 19 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed, 6.35 mm) | 100 | °C | ASTM D648 |
| Vicat Softening Temperature | 108 | °C | ASTM D1525 |
| CLTE - Flow (0 to 100°C) | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3200 µm) | 92.0 | % | ASTM D1003 |
| Haze (3200 µm) | < 1.0 | % | ASTM D1003 |
| Yellowness Index (3.20 mm) | < 1.0 | YI | ASTM D1925 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ 540 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| Weifang Kingdom CPE135B | Weifang Kingdom Plastic Co., Ltd | CPE | Weifang Kingdom |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 4215 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| Karina IVORY PVC COMPOUND -E 818-35/ 1-Y-SN-ERM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polychim HL10XF | Polychim Industrie S.A.S. | PP Homopolymer | Polychim |