LNP™ THERMOCOMP™ PF008S compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CoBRZr_LNPTHERMOCOMPPF008Scompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP PF008S is a compound based on Polyamide 6 resin containing Glass Fiber. Added features include: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound PF008S Product reorder name: PF008S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.46 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.90 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 182 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.9 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 10900 | MPa | ISO 178 |
| Flexural Stress | 273 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 16 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 88 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, unannealed, 64.0mm span | 217 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 204 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 9.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 1.8E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 249 - 260 | °C | |
| Middle Temperature | 266 - 277 | °C | |
| Front Temperature | 277 - 288 | °C | |
| Processing (Melt) Temp | 266 - 277 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® AG2677 | Covestro - Polycarbonates | PC | Makrolon® |
| Premier LD02329 - A | Premier Polymers, LLC. | LDPE | Premier |
| Wellamid® GF14-60 XE-NBK1 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| Bergamid™ B700 G15 H BK041 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Sylvin 6930X06 Green 3200 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |