ARCEL® LD (3.00 pcf)
| Category: | PS+PE , Polystyrene + PE |
| Manufacturer: | NOVA Chemicals |
| Trademark: | ARCEL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xzAwGr_ARCEL-LD-3-00-pcf-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ARCEL® LD (3.00 pcf) is a Polystyrene + PE (PS+PE) material. It is available in North America for foam processing. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.0481 | g/cm³ | ASTM D3575 |
| Particle Size - 98% | 0.900 to 2.00 | mm | |
| VOC Content | |||
| Pentane | 7.5 | % | |
| Plasticizer | 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain | 8.4 | % | ASTM C203 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture | 432 | N | ASTM D3763 |
| Tear Strength - at Maximum Load | 3.9 | kN/m | ASTM D3575 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 0.650 | MPa | ASTM D3575 |
| Flexural Strength | ASTM C203 | ||
| -- | 0.740 | MPa | |
| 5.0% Strain | 0.699 | MPa | |
| Compressive Strength | ASTM D3575 | ||
| 10% Strain | 0.330 | MPa | |
| 25% Strain | 0.380 | MPa | |
| 50% Strain | 0.462 | MPa | |
| 75% Strain | 0.957 | MPa |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 60 | mm/min | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYVIN® PVC 7026D | A. Schulman Inc. | PVC, Unspecified | POLYVIN® |
| THERMOLAST® K TF6BTL (Series: FC/AP) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Novamid® 1020A7 | DSM Engineering Plastics | Nylon 6 | Novamid® |
| ALFATER XL® A70I 4FC0000 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| Expandable PS RF33W | INEOS Styrenics International SA | PS (EPS) | Expandable PS |