Lucet® HI-520
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lucet® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Co7eV4_Lucet-HI-520.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lucet® HI-520 is an Acetal (POM) Copolymer material. It is available in North America for injection molding. Important attributes of Lucet® HI-520 are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 2.0 to 2.2 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 39.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 150 | % | ASTM D638 |
| Flexural Modulus | 1180 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 49.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 98 | J/m | |
| 23°C | 250 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 125 | °C | |
| 1.8 MPa, Unannealed | 75.0 | °C | |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.794 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Rear Temperature | 160 to 180 | °C | |
| Middle Temperature | 180 to 200 | °C | |
| Front Temperature | 190 to 200 | °C | |
| Nozzle Temperature | 190 to 210 | °C | |
| Processing (Melt) Temp | 190 to 200 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 39.2 to 68.6 | MPa | |
| Back Pressure | 3.92 to 7.84 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXALEN™ PPH329B20 | SAX Polymers | PP Homopolymer | SAXALEN™ |
| Tecomid® NB40 GR30 NL XA70 | Eurotec Engineering Plastics | Nylon 6 | Tecomid® |
| Spartech Polycom EP6333 B1 | Spartech Polycom | PP, Unspecified | Spartech |
| Gallonprene® GP200-15 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Kumho PPG 3601 | Korea Kumho Petrochemical Co., Ltd. | POP | Kumho PPG |