AEI SX490:CM401 and SX490:CM401-2
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | AEI Compounds Limited |
| Trademark: | AEI |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CbtkDG_AEI-SX490-CM401-and-SX490-CM401-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
UV stabilized silane crosslinkable polyethylene compound for aerial cables This is a silane crosslinkable polyethylene compound, curable by exposure to moist conditions, and possessing excellent extrusion properties at high output rates. The graft component SX490 is mixed with a crosslinking catalyst masterbatch CM401 or CM401-2 generally in the ratio 95:5. The compound contains 2.5% carbon and has been specially developed for insulated "overhead" or aerial cables of the bunched type, and enables full compliance with the German specification VDE 0274. It is advisable to use CM401-2 for less than 1mm thin wall applications; this is normally added at 10% to 90% graft. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | BS 2782 620A |
| Carbon Black Content | 2.5 | % | BS 2782 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 17.0 | MPa | IEC 60811-1-1 |
| Tensile Strain (Break) | 380 | % | IEC 60811-1-1 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength (135°C, 168 hr) | 5.0 | % | IEC 60811-1-2 |
| Change in Tensile Strain at Break (135°C, 168 hr) | -5.0 | % | IEC 60811-1-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 1 | IEC 60811-2-1 | ||
| Elongation under load, 20N/cm² : 200°C | % | IEC 60811-2-1 | |
| Permanent elongation after cooling | 0.0 | % | IEC 60811-2-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Power factor- 50Hz (23°C) | 8.00E-4 | IEC 60250 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 200 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (20°C) | > 1.0E+16 | ohms·cm | IEC 60502 |
| Relative Permittivity (23°C, 50 Hz) | 2.70 | IEC 60250 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 130 | °C | |
| Cylinder Zone 2 Temp. | 150 | °C | |
| Cylinder Zone 3 Temp. | 170 | °C | |
| Cylinder Zone 4 Temp. | 190 | °C | |
| Die Temperature | 210 | °C |
| Extrusion instructions |
|---|
| Most modern thermoplastic extruders will process SX490:CM401 & CM401-2 compounds, particularly if a screw suitable for polyethylene extrusion is available. |
| Note Message | |
|---|---|
| 1 . | Cure assessment by hot set test (forced cured at 80°C in water) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ABS F5330G20 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Network Polymers PP PPB 25 0216 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| ENSOFT SO-160-80A | ENPLAST, a Ravago Group Company | TPE | ENSOFT |
| Hostacom X 4305 HL86 105107 | LyondellBasell Industries | PP Copolymer | Hostacom |
| LUVOCOM® 94-8839/ES | LEHVOSS Group | LDPE | LUVOCOM® |