Hostacom X 4305 HL86 105107
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hFg0fw_HostacomX4305HL86105107.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostacom X 4305 HL86 105107 is a 22% talc filled PP copolymer, with good stiffness, good toughness and superior UV resistance. Product is available as a customized color matched, pellet form. This grade is delivered in 105107 color version. This grade is not intended for medical, pharmaceutical, food and drinking water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.04 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 27.0 | MPa | ISO 527-2 |
| Flexural Modulus 1(23°C) | 2300 | MPa | ISO 178/A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 148 | °C | ISO 306/A |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POWERSIL® 732 CS A/B | Wacker Chemie AG | Silicone | POWERSIL® |
| Safron® R702-40RNA | Safripol (PTY) LTD | PP Random Copolymer | Safron® |
| Nipol® SBR 1739 | Zeon Corporation | SBR, Emulsion | Nipol® SBR |
| Fainplast PVC GS 58 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Karina CLEAR PVC COMPOUND -E 80/306-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Rigid | Karina |