Reny® 4511
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CXdpGZ_Reny-4511.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Reny® 4511 is a Polyarylamide (PARA) material filled with 40% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Reny® 4511 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.77 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/3.8 kg) | 1.8 | -- | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (280°C/3.8 kg) | 1.00 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.35 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 0.060 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.70 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 20900 | 20600 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 130 | 125 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.60 | 0.80 | % | ISO 527-2 |
| Flexural Modulus | 22200 | 22000 | MPa | ISO 178 |
| Flexural Stress | 215 | 208 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.9 | 8.9 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 12 | 12 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 234 | 232 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 223 | 218 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | |||
| Flow | 8.0E-6 | -- | cm/cm/°C | |
| Transverse | 4.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 5.0E+3 | 4.0E+4 | ohms | IEC 60093 |
| Volume Resistivity | 3.0E+2 | 7.0E+8 | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 265 | °C | |
| Front Temperature | 270 | °C | |
| Nozzle Temperature | 270 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Texalan® 4 Series 485A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 4 Series |
| Toyolac® 700 X01 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| Cawiton® SN960 | Wittenburg B.V. | SEBS | Cawiton® |
| Dynaprene® 1065A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| Plexiglas® Heatresist hw55 | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |