Ecoflex® F Blend C1200
| Category: | Copolyester , Copolyester |
| Manufacturer: | BASF Corporation |
| Trademark: | Ecoflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CV2EEk_Ecoflex-F-Blend-C1200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ecoflex® F Blend C1200 is our biodegradable, statistical, aliphatic-aromatic copolyester based on the monomers 1,4-butanediol, adipic acid and terephthalic acid in the polymer chain. ecoflex® F Blend C1200 will biodegrade to the basic monomers 1,4-butanediol, adipic acid and terephthalic acid and eventually to carbon dioxide, water and biomass when metabolized in the soil or compost under standard conditions. ecoflex® F Blend C1200 has properties similar to PE-LD because of its high molecular weight and its long chain branched molecular structure. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 to 1.27 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.7 to 4.9 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 2.50 to 4.50 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 32 | ISO 868 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 50 µm, Blown Film | 36.0 | MPa | |
| TD : Break, 50 µm, Blown Film | 45.0 | MPa | |
| MD : 50 µm, Blown Film | 35.0 | MPa | |
| TD : 50 µm, Blown Film | 44.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm, Blown Film | 560 | % | |
| TD : Break, 50 µm, Blown Film | 710 | % | |
| Oxygen Transmission Rate (23°C, 0% RH, 50 µm, Blown Film) | 1200 | cm³/m²/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (23°C, 85% RH, 50 µm, Blown Film) | 140 | g/m²/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 91.0 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 110 to 120 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (50.0 µm, Blown Film) | 82.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Failure Energy - Dyna Test 1(50.0 µm) | 240 | J/cm | DIN 53373 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® A30B041 | Polyram Ram-On Industries | Nylon 66 | Polytron® |
| Santoprene™ 8281-45MED | ExxonMobil Chemical | TPV | Santoprene™ |
| Nipol® SBR NS310S | Zeon Corporation | SBR, Solution | Nipol® SBR |
| EVICOM™ GA4/130 | INEOS Compounds | PVC, Flexible | EVICOM™ |
| LUVOCOM® 1-1120 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |