SCHULAMID® XM GF 50 BLACK
| Category: | Nylon 66+Nylon 6I/6T , Polyamide 66 + PA 6I/6T |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C2hGAK_SCHULAMID-XM-GF-50-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50% glassfiber reinforced semi-aromatic Polyamide Compound with excellent rigity and strength, also if conditioned. Able for Substitution Die Cast Metal. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.59 | -- | g/cm³ | ISO 1183/A |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 3.5 to 4.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.1 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 931/30) | 290 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 17500 | 16500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 250 | 220 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus | 16400 | -- | MPa | ISO 178 |
| Flexural Stress 1 | 380 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ||||
| -30°C | 15 | -- | kJ/m² | ISO 179/1eC |
| 23°C | 17 | 17 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 95 | -- | kJ/m² | |
| 23°C | 110 | 100 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 245 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 225 | -- | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (1.00 mm) | < 100 | -- | mm/min | ISO 3795 |
| Flame Rating (0.800 mm) | HB | -- | UL 94, IEC 60695-11-10, -20 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefanyl® VR VRGR 364 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | tefanyl® VR |
| UNIVAL™ DMDG-6240 NT 7 | The Dow Chemical Company | HDPE | UNIVAL™ |
| Badamid® LB70 GF25 | Bada AG | Nylon 6 | Badamid® |
| Elastron® G G401.A55.N | Elastron USA, Inc. | SEBS | Elastron® G |
| Karina GRAY PVC COMPOUND 740-DA-18/339-A-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |