LNP™ LUBRILOY™ R2000 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bpgt4G_LNPLUBRILOYR2000compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY R2000 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRILOY* Compound R Product reorder name: R2000 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 1.8 - 2.2 | % | ASTM D955 |
| Transverse flow : 24 hours | 2.1 - 3.1 | % | ASTM D955 |
| Water Absorption (24 hr, 50% RH) | 0.25 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2410 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield | 56.9 | MPa | ASTM D638 |
| Fracture | 55.4 | MPa | ASTM D638 |
| Fracture | 53.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 14 | % | ASTM D638 |
| Fracture | 27 | % | ASTM D638 |
| Fracture | 32 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2320 | MPa | ASTM D790 |
| -- | 2000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 82.2 | MPa | ASTM D790 |
| -- | 65.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.36 | ASTM D3702 Modified | |
| With Self-Static | 0.27 | ASTM D3702 Modified | |
| Wear Factor - Washer | 50.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 62 | J/m | ASTM D256 |
| 23°C 2 | 6.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1700 | J/m | ASTM D4812 |
| 23°C 3 | 140 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 77.8 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 85.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 7.7E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 271 - 282 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2910-85 Clear | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Xuchuan XCW-8060DY | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| ADENE NTQA | A.D. Compound spa | PP Homopolymer | ADENE |
| Braskem PE GF4950HS | Braskem | HDPE Copolymer | Braskem PE |
| KumhoSunny PC HCG2530HG | Shanghai KumhoSunny Plastics Co., Ltd. | PC | KumhoSunny PC |